Piezoelectric polymeric bicomponent fibers produced by melt spinning

Lund, AnjaHögskolan i Borås,Institutionen Textilhögskolan,Chalmers tekniska högskola,Chalmers University of Technology,University of Borås, Sweden; Chalmers University of Technology, Sweden (författare)

Melt spinning of a novel piezoelectric bicomponent fiber, with poly(vinylidene fluoride) as the electroactive sheath component, has been demonstrated. An electrically conductive compound of carbon black (CB) and high density polyethylene was used as core material, working as an inner electrode. A force sensor consisting of a number of fibers embedded in a soft CB/polyolefin elastomer matrix was manufactured for characterization. The fibers showed a clear piezoelectric effect, with a voltage output (peak-to-peak) of up to 40 mV under lateral compression. This continuous all-polymer piezoelectric fiber introduces new possibilities toward minimal single fiber sensors as well as large area sensors produced in standard industrial weaving machines.

Johansson, ChristerRISE,Acreo(Swepub:ri)ChristerJoh@ri.se (författare)
Johansson, Christer (författare)
Haagensen, DanielRISE,IVF,Chalmers University of Technology, Sweden(Swepub:cth)haagense (författare)
Hagström, Bengt,1954RISE,IVF,Chalmers University of Technology, Sweden(Swepub:cth)bengtha (författare)
Högskolan i BoråsInstitutionen Textilhögskolan (creator_code:org_t)

Ingår i:Journal of Applied Polymer Science: Wiley Periodicals, Inc.126:2, s. 490-5000021-89951097-4628

Av författaren/redakt...: Lund, Anja; Johansson, Chris ...; Haagensen, Danie ...; Hagström, Bengt, ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Pappers massa oc ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Textil gummi och ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.