Influence of grain refinement on slurry formation and surface segregation in semi-solid Al-7Si-0.3Mg castings

• This study aims to evaluate the effect of grain refinement on slurry formation and surface segregation in semi-solid castings produced by the Rheometal™ process. The effect of two grain refiners, Al-8B and Al-5Ti-1B, on the slurry α-Al grain size, shape factor and solid fraction was evaluated. The results suggest that the addition of a grain refiner can affect the solid fraction obtained in the RheometalTM process and, consequently, reduce the solute content near the casting surface. Grain refiner addition resulted in a larger fraction of α-Al grains ≤ 60 µm for the refined alloys compared with the unrefined alloy. Additionally, the growth of α-Al slurry globules was greater for the unrefined alloy compared with the refined alloy during solidification in the die-cavity. A more homogeneous and finer microstructure was observed near the surface in the grain-refined castings compared with the unrefined castings. Evidence of significant liquid penetration was identified in some α-Al globules, indicating that disintegration of α-Al globules may occur during the Rheometal™ casting process.

Subject headings

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Publication and Content Type

ref (subject category)

art (subject category)