Experimental and modelling study of the effect of tempering on the susceptibility to environment-assisted cracking of AISI 420 martensitic stainless steel

• The resistance to environment-assisted cracking (EAC) of AISI 420 martensitic stainless steel (MSS) was investigated in 0.3 M NaCl solution (room temperature) at constant loads for 30 days. The steel tempered at 250 degrees C was superior to the 500 degrees C-temper, which showed corrosion pits favouring cracking. The fracture surface showed faceted grains, cleavage, striations, and inter- and transgranular cracks, suggesting a mixed stress corrosion cracking (SCC) and hydrogen embrittlement (HE) mechanism as the cause for EAC. Finite element modelling (FEM) indicated strain/stress localization at the mouth of deep pits and at the wall of shallow pits, displaying the favoured locations for pit-to-crack transition.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Nyckelord

Martensitic stainless steel

Residual stress

Tempering

Environment-assisted cracking

Pit-to-crack transition