Elemental distribution and fracture properties of magnetron sputtered carbon supersaturated tungsten films
-
- Fritze, Stefan (författare)
- Uppsala universitet,Oorganisk kemi,Uppsala University
-
- Hahn, R. (författare)
- Institute of Materials Science and Technology, TU Wien, A-1060 Vienna, Austria,Technische Universität Wien,Vienna University of Technology
-
- Aboulfadl, Hisham, 1986 (författare)
- Department of Physics, Chalmers University of Technology, SE-412 96 Göteborg, Sweden,Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Johansson, Fredrik (författare)
- KTH,Tillämpad fysikalisk kemi,Division of Applied Physical Chemistry, Department of Chemistry, KTH – Royal Institute of Technology, SE-100 44 Stockholm, Sweden; Institute Methods and Instrumentation for Synchrotron Radiation Research PS-ISRR, Helmholtz-Zentrum Berlin für Materialien und Energie, Albert-Einstein-Straße 15, 12489 Berlin, Germany; Institut für Physik und Astronomie, Universität Potsdam, Karl-Liebknecht-Strasse 24-25, 14476 Potsdam, Germany,Universität Potsdam,University of Potsdam,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH),Helmholtz Zentrum,Helmholtz Center
-
- Lindblad, Rebecka, Dr, 1984- (författare)
- Uppsala universitet,Institutionen för kemi - Ångström,Uppsala University
-
- Böör, Katalin (författare)
- Uppsala universitet,Oorganisk kemi,Uppsala University
-
- Lindblad, Andreas, Lecturer, 1978- (författare)
- Uppsala universitet,Energimaterialens fysik,Uppsala University
-
- Berggren, Elin (författare)
- Uppsala universitet,Energimaterialens fysik,Uppsala University
-
- Kühn, D. (författare)
- Institute Methods and Instrumentation for Synchrotron Radiation Research PS-ISRR, Helmholtz-Zentrum Berlin für Materialien und Energie, Albert-Einstein-Straße 15, 12489, Berlin, Germany, Albert-Einstein-Straße 15,Helmholtz Zentrum,Helmholtz Center
-
- Leitner, T. (författare)
- Institute Methods and Instrumentation for Synchrotron Radiation Research PS-ISRR, Helmholtz-Zentrum Berlin für Materialien und Energie, Albert-Einstein-Straße 15, 12489, Berlin, Germany, Albert-Einstein-Straße 15,Helmholtz Zentrum,Helmholtz Center
-
- Osinger, Barbara (författare)
- Uppsala universitet,Oorganisk kemi,Uppsala University
-
- Lewin, Erik, Dr. 1979- (författare)
- Uppsala universitet,Oorganisk kemi,Uppsala University
-
- Jansson, Ulf, 1960- (författare)
- Uppsala universitet,Oorganisk kemi,Uppsala University
-
- Mayrhofer, P. H. (författare)
- Institute of Materials Science and Technology, TU Wien, A-1060 Vienna, Austria,Technische Universität Wien,Vienna University of Technology
-
- Thuvander, Mattias, 1968 (författare)
- Department of Physics, Chalmers University of Technology, SE-412 96 Göteborg, Sweden,Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2024
- 2024
- Engelska.
-
Ingår i: Surface & Coatings Technology. - : Elsevier BV. - 0257-8972 .- 1879-3347. ; 477
- Relaterad länk:
-
https://doi.org/10.1...
-
visa fler...
-
https://uu.diva-port... (primary) (Raw object)
-
https://research.cha... (primary) (free)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The combination of strength and toughness is a major driving force for alloy design of protective coatings, and nanocrystalline tungsten (W)-alloys have shown to be promising candidates for combining strength and toughness. Here we investigate the elemental distribution and the fracture toughness of carbon (C) alloyed W thin films prepared by non-reactive magnetron sputtering. W:C films with up to ~4 at.% C crystallize in a body-centered-cubic structure with a strong 〈hh0〉texture, and no additional carbide phases are observed in the diffraction pattern. Atom probe tomography and X-ray photoelectron spectroscopy confirmed the formation of such a supersaturated solid solution. The pure W film has a hardness ~13 GPa and the W:C films exhibit a peak hardness of ~24 GPa. In-situ micromechanical cantilever bending tests show that the fracture toughness decreases from ~4.5 MPa·m1/2 for the W film to ~3.1 MPa·m1/2 for W:C films. The results show that C can significantly enhance the hardness of W thin films while retaining a high fracture toughness.
Ämnesord
- NATURVETENSKAP -- Kemi -- Oorganisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Tribologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Tribology (hsv//eng)
Nyckelord
- Atom probe tomography
- Fracture toughness
- PVD
- Tungsten
- XPS
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Fritze, Stefan
-
Hahn, R.
-
Aboulfadl, Hisha ...
-
Johansson, Fredr ...
-
Lindblad, Rebeck ...
-
Böör, Katalin
-
visa fler...
-
Lindblad, Andrea ...
-
Berggren, Elin
-
Kühn, D.
-
Leitner, T.
-
Osinger, Barbara
-
Lewin, Erik, Dr. ...
-
Jansson, Ulf, 19 ...
-
Mayrhofer, P. H.
-
Thuvander, Matti ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Oorganisk kemi
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Maskinteknik
-
och Tribologi
- Artiklar i publikationen
-
Surface & Coatin ...
- Av lärosätet
-
Kungliga Tekniska Högskolan
-
Uppsala universitet
-
Chalmers tekniska högskola