Time-delayed transformation of defects in zinc oxide layers grown along the zinc-face using a hydrothermal technique

Klason, Peter, 1977 (författare): Gothenburg University,Göteborgs universitet,Institutionen för fysik (GU),Department of Physics (GU)

Nour, Omer (författare): Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan

Ul Wahab, Qamar (författare): Linköpings universitet,Halvledarmaterial,Tekniska högskolan

Willander, Magnus (författare): Gothenburg University,Göteborgs universitet,Linköpings universitet,Institutionen för teknik och naturvetenskap,Tekniska högskolan,Institutionen för fysik (GU),Department of Physics (GU)

(creator_code:org_t)

AIP Publishing, 2009
2009
Engelska.
Ingår i: JOURNAL OF APPLIED PHYSICS. - : AIP Publishing. - 0021-8979 .- 1089-7550. ; 105:12, s. 123510-

Relaterad länk:: https://urn.kb.se/re...; visa fler...; https://doi.org/10.1...; https://gup.ub.gu.se...; visa färre...

Abstract Ämnesord

Stäng

A study of deep level defects in a hydrothermally grown, intrinsically n-type zinc oxide (ZnO) device has been carried out using conventional deep level transient spectroscopy (DLTS). Performed under variable measurement conditions, DLTS demonstrates two electron trap levels, E-1 (dominant) and E-2, with activation energies E-c-0.22 +/- 0.02 eV and E-c-0.47 +/- 0.05 eV, respectively. A time-delayed transformation of shallow donor defects zinc(interstitial) and vacancy(oxygen) (Zn-i-VO) into the E-1 level has been observed. While the x-ray diffraction measurements reveal that the preferred direction of ZnO growth is along the (10 (1) over bar0) plane, i.e., the (Zn-i-V-O) complex, it is assumed that the (Zn-i-V-O) complex is transformed into a zinc antisite (Zn-O) under favorable conditions. As a result, the free carrier concentration decreases with increasing trap concentration. Henceforth, the E-1 level exhibiting the increase in concentration is attributed to ZnO.

Av författaren/redakt...: Noor, Hadia; Klason, Peter, 1 ...; Nour, Omer; Ul Wahab, Qamar; Asghar, M.; Willander, Magnu ...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.