Esmaeilzadeh, SaeidStockholms universitet,Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi (author)

The present work explores the glass-forming region in the Ca–Si–O–N system, particularly in the N-rich part of the system. Bulk oxynitride glasses in the Ca–Si–O–N system were prepared by melting mixtures of CaH2, SiO2 and Si3N4 powders in a nitrogen atmosphere at 1500–1650 °C. The glasses were characterized by X-ray powder diffraction, differential thermal analysis, scanning electron microscopy and transmission electron microscopy. Glass compositions were calculated from analyses obtained by energy dispersive X-ray (EDX) spectroscopy and combustion analysis, for cation and anion compositions, respectively. The glasses were found to be X-ray amorphous and gray to black in color. The glasses retain up to 58 e/o of nitrogen and 42 e/o of calcium. The glass formation depends on reaction kinetics and the precursor used. A strong exothermic reaction is observed at 850–1000 °C, leading to formation of amorphous and crystalline oxynitride phases that melt at high temperatures upon further heating. Glass transition temperatures (Tg) were observed to vary between 798 °C and 1050 °C, and crystallization occurs typically 130 °C above the glass transition temperature. The glass densities vary between 2.79 g/cm3 and 3.25 g/cm3.

Grins, J.Stockholms universitet,Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi (author)
Sharafat, AliStockholms universitet,Institutionen för fysikalisk kemi, oorganisk kemi och strukturkemi(Swepub:su)ashar (author)
Stockholms universitetInstitutionen för fysikalisk kemi, oorganisk kemi och strukturkemi (creator_code:org_t)

In:Journal of the European Ceramic Society: Elsevier BV28:14, s. 2659-26640955-22191873-619X

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.