Helium Bubble Growth in He + Ions Implanted 304L Stainless Steel Processed by Laser Powder Bed Fusion During Post-Irradiation Annealing at 600 °C
-
- Liu, Hui (författare)
- University of Shanghai for Science and Technology
-
- Min, Shiling (författare)
- University of Shanghai for Science and Technology
-
- Jiang, Menglei (författare)
- University of Shanghai for Science and Technology
-
visa fler...
-
- Chu, Fuzhong (författare)
- University of Shanghai for Science and Technology
-
- Li, Ying (författare)
- University of Shanghai for Science and Technology
-
- Chen, Zhuoer, 1989 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Zhang, Kai (författare)
- Monash University,University of Shanghai for Science and Technology
-
- Hou, Juan (författare)
- University of Shanghai for Science and Technology,China Nuclear Power Engineering Co., Ltd.
-
- Huang, Aijun (författare)
- Monash University
-
visa färre...
-
(creator_code:org_t)
- 2022-02-16
- 2022
- Engelska.
-
Ingår i: Acta Metallurgica Sinica (English Letters). - : Springer Science and Business Media LLC. - 1006-7191 .- 2194-1289. ; 35:9, s. 1509-1518
- Relaterad länk:
-
https://research.cha...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The abundancy of defect sinks in the microstructure of laser powder bed fusion (LPBF) processed austenitic stainless steels was found to be beneficial for helium resistance. In the current study, the influence of the novel microstructure in LPBF processed 304L on the helium bubble growth behaviour was investigated using transmission electron microscopy in samples implanted with He+ ion and post-irradiation annealing treated at 600 °C for 1 h. Two variants of LPBF processed 304L samples were used, one in as-built condition and the other solution-annealed. The comparison between the two samples indicated that the helium bubble growth was inhibited and remained stable in the as-built sample but coarsened significantly in the solution-annealed sample. The sub-grain boundaries and oxide nano-inclusions acted as defect sinks to trap helium atoms and inhibited the growth of helium bubble in the as-built sample under the post-irradiation annealing conditions used.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Laser powder bed fusion
- Nano oxide inclusions
- Irradiation tolerance
- Stainless steel
- Helium bubble growth
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Liu, Hui
-
Min, Shiling
-
Jiang, Menglei
-
Chu, Fuzhong
-
Li, Ying
-
Chen, Zhuoer, 19 ...
-
visa fler...
-
Zhang, Kai
-
Hou, Juan
-
Huang, Aijun
-
visa färre...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Bearbetnings yt ...
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Annan materialte ...
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Metallurgi och m ...
- Artiklar i publikationen
-
Acta Metallurgic ...
- Av lärosätet
-
Chalmers tekniska högskola