Characterisation of EBM-built shelled samples of Ti6Al4V compacted by HIP

Rännar, Lars-Erik (författare): Mittuniversitetet,Avdelningen för kvalitetsteknik, maskinteknik och matematik,Sports Tech Research Centre,Mid Sweden University

Koptyug, Andrey (författare): Mittuniversitetet,Avdelningen för kvalitetsteknik, maskinteknik och matematik,Sports Tech Research Centre,Mid Sweden University

Leicht, Alexander, 1987 (författare): Chalmers University of Technology, Sweden,Chalmers tekniska högskola,Quintus Technologies AB

Vattur Sundaram, Maheswaran, 1987 (författare): Chalmers University of Technology, Sweden,Chalmers tekniska högskola

Hryha, Eduard, 1980 (författare): Chalmers University of Technology, Sweden,Chalmers tekniska högskola

Nyborg, Lars, 1958 (författare): Chalmers University of Technology, Sweden,Chalmers tekniska högskola

Ahlfors, M. (författare): Quintus Technologies, Sweden,Quintus Technologies, Västerås

(creator_code:org_t)

European Powder Metallurgy Association (EPMA), 2016
2016
Engelska.
Ingår i: World PM 2016 Congress and Exhibition. - : European Powder Metallurgy Association (EPMA). - 9781899072484

Relaterad länk:: https://urn.kb.se/re...; visa fler...; https://urn.kb.se/re...; https://research.cha...; visa färre...

Abstract Ämnesord

Stäng

Compaction of additively manufactured Ti6Al4V components by Hot Isostatic Pressing (HIP) is often applied to eliminate porosity, producing fully dense material. In the present work shelled samples produced by Electron Beam Melting with the Arcam process (EBM) were compacted by HIP to produce fully dense samples. Cylindrical samples were studied. The walls of the cylinders were built with EBM, and the powder from the process was left uncompacted inside the cylinders. Samples with different wall thicknesses were produced. The samples were thereafter subjected to a HIP compaction. The critical wall thicknesses needed for compaction were evaluated, and the microstructures characterized. The results show that fully dense samples, with very fine microstructures, are possible.

TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Av författaren/redakt...: Frisk, Karin; Rännar, Lars-Eri ...; Koptyug, Andrey; Petterson, Nikla ...; Persson, Daniel; Leicht, Alexande ...; visa fler...; Vattur Sundaram, ...; Hryha, Eduard, 1 ...; Nyborg, Lars, 19 ...; Ahlfors, M.; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.