Conducting grain boundaries in the high-dielectric-constant ceramic CaCu3Ti4O12

To clarify the electrical property of grain boundaries, the fine-grained ceramics CaCu3Ti4O12 have been treated with the hydrofluoric acid to remove the parts of grain boundaries. The dielectric response difference between the etched samples and the pristine ones indicates that the ceramic CaCu3Ti4O12 consists of insulating or semiconducting grains with conducting grain boundaries. Therefore, the giant dielectric phenomenon is supposed not to derive from the grain boundary barrier layer capacitance effect. The possible mechanism is discussed. (c) 2007 American Institute of Physics.

Li, G. L.Nanjing University, Peoples R China (författare)
Gao, FengLinköpings universitet,Biomolekylär och Organisk Elektronik,Tekniska högskolan(Swepub:liu)fenga88 (författare)
Liu, J.Nanjing University, Peoples R China (författare)
Liu, J. M.Nanjing University, Peoples R China (författare)
Zhu, J. S.Nanjing University, Peoples R China (författare)
Nanjing University, Peoples R ChinaBiomolekylär och Organisk Elektronik (creator_code:org_t)

Ingår i:Journal of Applied Physics: American Institute of Physics (AIP)101:7, s. 074101-0021-89791089-7550

Av författaren/redakt...: Chen, K.; Li, G. L.; Gao, Feng; Liu, J.; Liu, J. M.; Zhu, J. S.

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.