Sökning: WFRF:(Wickman Marie) > Nanometer-thick fil...

LIBRIS Formathandbok  (Information om MARC21)
FältnamnIndikatorerMetadata
00003690naa a2200457 4500
001oai:research.chalmers.se:6b3a108f-b159-40a6-9887-c271fe8c9dab
003SwePub
008171007s2007 | |||||||||||000 ||eng|
009oai:DiVA.org:kth-7243
0247 a https://research.chalmers.se/publication/616882 URI
0247 a https://doi.org/10.1016/j.electacta.2006.12.0022 DOI
0247 a https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-72432 URI
040 a (SwePub)cthd (SwePub)kth
041 a engb eng
042 9 SwePub
072 7a art2 swepub-publicationtype
072 7a ref2 swepub-contenttype
1001 a Ekström, Henriku KTH,Tillämpad elektrokemi4 aut0 (Swepub:kth)u101temd
2451 0a Nanometer-thick films of titanium oxide acting as electrolyte in the polymer electrolyte fuel cell
264 1b Elsevier BV,c 2007
500 a QC 20100706
520 a 0–18 nm-thick titanium, zirconium and tantalum oxide films are thermally evaporated on Nafion 117 membranes, and used as thin spacer electrolyte layers between the Nafion and a 3 nm Pt catalyst film. Electrochemical characterisation of the films in terms of oxygen reduction activity, high frequency impedance and cyclic voltammetry in nitrogen is performed in a fuel cell at 80 ◦C and full humidification. Titanium oxide films with thicknesses up to 18 nm are shown to conduct protons, whereas zirconium oxide and tantalum oxide block proton transport already at a thickness of 1.5 nm. The performance for oxygen reduction is higher for a bi-layered film of 3 nm platinum on 1.5 or 18 nm titanium oxide, than for a pure 3 nm platinum film with no spacer layer. The improvement in oxygen reduction performance is ascribed to a higher active surface area of platinum, i.e. no beneficial effect of combining platinum with zirconium, tantalum or titanium oxides on the intrinsic oxygen reduction activityis seen. The results suggest that TiO2 may be used as electrolyte in fuel cell electrodes, and that low-temperature proton exchange fuel cells could be possible using TiO2 as electrolyte.
650 7a NATURVETENSKAPx Kemix Oorganisk kemi0 (SwePub)104042 hsv//swe
650 7a NATURAL SCIENCESx Chemical Sciencesx Inorganic Chemistry0 (SwePub)104042 hsv//eng
653 a Oxygen reduction
653 a Titanium oxide
653 a Proton conduction
653 a Fuel cell
653 a Thermal evaporation
653 a Electrochemistry
7001 a Wickman, Björn,d 1980u Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg4 aut0 (Swepub:cth)k01wibj
7001 a Gustavsson, Marie,d 1969u Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg4 aut
7001 a Hanarp, Per,d 1974u Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg4 aut0 (Swepub:cth)hanarp
7001 a Eurenius, Lisa,d 1977u Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg4 aut0 (Swepub:cth)eurenius
7001 a Olsson, Eva,d 1960u Chalmers tekniska högskola,Chalmers University of Technology,Chalmers tekniska högskola, Göteborg4 aut0 (Swepub:cth)f10eva
7001 a Lindbergh, Göranu KTH,Tillämpad elektrokemi4 aut0 (Swepub:kth)u13qsu09
7102 a KTHb Tillämpad elektrokemi4 org
7730 t Electrochimica Actad : Elsevier BVg 52:12, s. 4239-4245q 52:12<4239-4245x 0013-4686x 1873-3859
8564 8u https://research.chalmers.se/publication/61688
8564 8u https://doi.org/10.1016/j.electacta.2006.12.002
8564 8u https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-7243

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy