Effect of low temperature on tensile properties of AlCoCrFeNi2.1 eutectic high entropy alloy

Sheikh, Saad Ahmed, 1987 (författare): Chalmers tekniska högskola,Chalmers University of Technology

Guo, Sheng, 1981 (författare): Chalmers tekniska högskola,Chalmers University of Technology

Clark, I. T. (författare)

Okawa, T. (författare)

(creator_code:org_t)

Elsevier BV, 2018
2018
Engelska.
Ingår i: Materials Chemistry and Physics. - : Elsevier BV. - 0254-0584. ; 210, s. 207-212

Relaterad länk:: https://research.cha...; visa fler...; https://doi.org/10.1...; visa färre...

Abstract Ämnesord

Stäng

The effect of low temperature on tensile properties of a AlCoCrFeNi 2.1 eutectic high entropy alloy (EHEA) was investigated in the present work. Transmission electron microscopy (TEM) showed that the initial as-cast microstructure consisted of B2 (ordered body centered cubic structure) and L1 2 (ordered face centered cubic structure) phases. Upon tensile testing at temperatures ranging from room temperature (RT) to −196 °C (77 K), the L1 2 phase became disordered, changing to a simple FCC (face centered cubic) crystal structure whereas the B2 phase maintained an ordered structure. An increase over 300 MPa was observed in the ultimate tensile strength (σ UTS ) of the −196 °C tensile tested sample compared to the room temperature tensile tested sample, while keeping almost similar amount of total elongation. TEM results indicated an increase in the dislocation activity in the FCC phase as well as B2 phase in the −196 °C tensile tested sample compared to the sample deformed at room temperature.

TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)

Av författaren/redakt...: Bhattacharjee, T ...; Zheng, Ruixiao; Chong, Yan; Sheikh, Saad Ahm ...; Guo, Sheng, 1981; Clark, I. T.; visa fler...; Okawa, T.; Wani, I. S.; Bhattacharjee, P ...; Shibata, Akinobu; Tsuji, N.; visa färre...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Annan materialte ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.