  • Wu, Jingnan,1994Aalborg Universitet,Aalborg University,Chalmers tekniska högskola,Chalmers University of Technology,Shandong University,Soochow University (författare)

Modulating the nanoscale morphology on carboxylate-pyrazine containing terpolymer toward 17.8% efficiency organic solar cells with enhanced thermal stability

  • Artikel/kapitelEngelska2022

Förlag, utgivningsår, omfång ...

  • Elsevier BV,2022

Nummerbeteckningar

  • LIBRIS-ID:oai:research.chalmers.se:9a02bebd-8ae7-41eb-aa09-14d677b8befb
  • https://doi.org/10.1016/j.cej.2022.137424DOI
  • https://research.chalmers.se/publication/530868URI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:art swepub-publicationtype
  • Ämneskategori:ref swepub-contenttype

Anmärkningar

  • It had been commonly accepted in the organic photovoltaic (OPV) community that subtle variations in the molecular structure of active layer materials would cause profound impacts on their aggregating structure and blend morphology and therefore the performance of such polymer solar cells (PSCs). Herein, we employed an electron-deficient building block 3,6-dithiophenyl-2-carboxylate pyrazine (DTCPz) for constructing one series of promising donor terpolymers of PMZ1, PMZ2, and PMZ3, respectively, gaining their relatively lower-lying highest occupied molecular orbital (HOMO) energy levels, more closed π-π stacking and enhanced crystallinity in thin films, and lower miscibility with acceptor Y6, in comparison with their parent polymer counterpart (namely PM6). Reaching DTCPz moieties up to 20% (mol/mol%) in its terpolymer composition, the resulting polymer (PMZ2) achieved more favorable phase separation with improved exciton dissociation, and charge transport and extraction. As a result, an outstanding fill factor of 77.2% and a promising power conversion efficiency of 17.8 % was achieved. Moreover, the corresponding device shows better thermal stability over the PM6-based one. This work suggests a facile method for significantly improving the thin film morphology of the active-layer materials via fine-tuning the chemical structure of electron-deficient units on the backbone of the wide bandgap donor polymer, therefore achieving enhanced photovoltaic performance and thermal stability for practical applications.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Guo, XiaShandong University,Soochow University (författare)
  • Xiong, MinghaiSoochow University (författare)
  • Xia, XinxinChinese University of Hong Kong (författare)
  • Li, Qi,1990Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)qili (författare)
  • Fang, JinSoochow University (författare)
  • Yan, XinSoochow University (författare)
  • Liu, QiSoochow University (författare)
  • Lu, XinhuiChinese University of Hong Kong (författare)
  • Wang, Ergang,1981Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)ergang (författare)
  • Yu, DonghongAalborg Universitet,Aalborg University (författare)
  • Zhang, MaojieShandong University,Soochow University (författare)
  • Aalborg UniversitetChalmers tekniska högskola (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Chemical Engineering Journal: Elsevier BV4461385-8947

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy