Synthesis of novel ...
Synthesis of novel aggregating comb-shaped polyethers for use as polymer electrolytes
-
- Jannasch, Patric (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
(creator_code:org_t)
- 2000-10-25
- 2000
- Engelska.
-
Ingår i: Macromolecules. - : American Chemical Society (ACS). - 0024-9297 .- 1520-5835. ; 33:23, s. 8604-8610
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Polyethers having well-defined comb-shaped architectures were prepared by using poly(4-hydroxystyrene) (PHSt) as a multifunctional initiator for graft polymerization of either ethylene oxide (EO) or a mixture of EO and propylene oxide (PO). The grafting process was performed in 1,4-dioxane using NaH as ionizer for the PHSt hydroxyl groups. The precursor PHSt was prepared by first polymerizing 4-tert-butoxystyrene, using butyllithium as initiator in THF at -60 degreesC, and then deprotecting the butoxy groups. Finally, the terminal hydroxyl groups of the polyether grafts were end-capped with hexadecanoyl units through esterification. The monomer addition sequence in the graft copolymerizations with the same EO/PO feed ratio proved to have a great influence on the crystallization temperature and the crystallinity of the grafts. Also, the end-capping was found to reduce the degree of crystallinity as compared to the corresponding uncapped polymers. Solid polymer electrolytes containing lithium triflate (LiSO3-CF3) salt had ambient temperature ion conductivities of similar to 10(-5) S/cm at [Li]/[O] = 0.025. Thermal analysis of the electrolytes showed that the polymers aggregated through phase separation of the hexadecanoyl chain ends.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)