Influence of Process Parameters on Reaction Products during Self-Propagating High-Temperature Synthesis of Porous NiTi
-
- Jarfors, A. E. W. (författare)
- Singapore Inst. of Mfg. Technology, Process Technology Division, Precision Metal Forming Group, Singapore
-
- Sim, G. C. (författare)
- Singapore Inst. of Mfg. Technology, Process Technology Division, Precision Metal Forming Group, Singapore
-
- San, T. E. (författare)
- Singapore Inst. of Mfg. Technology, Process Technology Division, Precision Metal Forming Group, Singapore
-
Singapore Inst of Mfg. Technology, Process Technology Division, Precision Metal Forming Group, Singapore (creator_code:org_t)
- 2003
- 2003
- Engelska.
-
Ingår i: Materials Science Forum. - 0255-5476 .- 1662-9752. ; 437-438, s. 475-478
- Relaterad länk:
-
http://www.scopus.co...
-
visa fler...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- NiTi is proposed to be a biomaterial suitable for bone replacements. Reactive synthesis, Self-Propagating High-Temperature Synthesis (SHS) of NiTi from Ni and Ti powder is a suitable method to produce porous structures to promote osseointegration. The influence of pressed density and ignition temperature on the reaction products formed is investigated. Porosity after pressing was 20%, 30% and 40 % and ignition temperatures were 400°C, 500°C and 600°C. The reaction products found were NiTi, as well as Ti2Ni and Ni3Ti, in addition to residual Ni and Ti. The amount of NiTi formed increases with ignition temperature, with a maximum at an initial porosity of 30% and ignition temperature of 600°C. This coincides with the minimum amount of residual Ni and Ti. The reaction imbalance is caused by the formation of Ti2Ni at high pressed densities and by a preferential nucleation of Ni3Ti, both suggested to be dominated by the effective contact area between the Ni and Ti particles after pressing.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- Bicmaterial
- Ni
- NiTi
- Phase Selection
- Reaction Synthesis
- Ti
- Reaction products
- Density measurement (specific gravity)
- High temperature effects
- Ignition
- Porosity
- Porous materials
- Reaction kinetics
- Synthesis (chemical)