Sökning: WFRF:(Talyzin Alexandr) > Hydrogen storage in...
Fältnamn | Indikatorer | Metadata |
---|---|---|
000 | 02796naa a2200409 4500 | |
001 | oai:DiVA.org:umu-109475 | |
003 | SwePub | |
008 | 150928s2015 | |||||||||||000 ||eng| | |
024 | 7 | a https://urn.kb.se/resolve?urn=urn:nbn:se:umu:diva-1094752 URI |
024 | 7 | a https://doi.org/10.1039/c5cc05474e2 DOI |
040 | a (SwePub)umu | |
041 | a engb eng | |
042 | 9 SwePub | |
072 | 7 | a ref2 swepub-contenttype |
072 | 7 | a art2 swepub-publicationtype |
100 | 1 | a Klechikov, Alexeyu Umeå universitet,Institutionen för fysik4 aut0 (Swepub:umu)alkl0012 |
245 | 1 0 | a Hydrogen storage in high surface area graphene scaffolds |
264 | c 2015 | |
264 | 1 | b Royal Society of Chemistry,c 2015 |
338 | a electronic2 rdacarrier | |
520 | a Using an optimized KOH activation procedure we prepared highly porous graphene scaffold materials with SSA values up to 3400 m2 g−1 and a pore volume up to 2.2 cm3 g−1, which are among the highest for carbon materials. Hydrogen uptake of activated graphene samples was evaluated in a broad temperature interval (77–296 K). After additional activation by hydrogen annealing the maximal excess H2 uptake of 7.5 wt% was obtained at 77 K. A hydrogen storage value as high as 4 wt% was observed already at 193 K (120 bar H2), a temperature of solid CO2, which can be easily maintained using common industrial refrigeration methods. | |
650 | 7 | a NATURVETENSKAPx Fysikx Den kondenserade materiens fysik0 (SwePub)103042 hsv//swe |
650 | 7 | a NATURAL SCIENCESx Physical Sciencesx Condensed Matter Physics0 (SwePub)103042 hsv//eng |
653 | a graphene hydrogen storage adsorption | |
653 | a Physical Chemistry | |
653 | a fysikalisk kemi | |
700 | 1 | a Mercier, Guillaumeu Umeå universitet,Institutionen för fysik4 aut0 (Swepub:umu)gume0003 |
700 | 1 | a Sharifi, Tivau Umeå universitet,Institutionen för fysik4 aut0 (Swepub:umu)tish0004 |
700 | 1 | a Baburin, Igor A.u Technische Universität Dresden, Theoretische Chemie, Bergstraße 66b, 01062 Dresden, Germany4 aut |
700 | 1 | a Seifert, Gotthardu Technische Universität Dresden, Theoretische Chemie, Bergstraße 66b, 01062 Dresden, Germany4 aut |
700 | 1 | a Talyzin, Alexandr V.,d 1969-u Umeå universitet,Institutionen för fysik4 aut0 (Swepub:umu)alta0001 |
710 | 2 | a Umeå universitetb Institutionen för fysik4 org |
773 | 0 | t Chemical Communicationsd : Royal Society of Chemistryg 51:83, s. 15280-15283q 51:83<15280-15283x 1359-7345x 1364-548X |
856 | 4 | u https://umu.diva-portal.org/smash/get/diva2:857221/FULLTEXT02.pdfx primaryx Raw objecty fulltext:preprint |
856 | 4 | u https://tud.qucosa.de/api/qucosa%3A36058/attachment/ATT-0/ |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:umu:diva-109475 |
856 | 4 8 | u https://doi.org/10.1039/c5cc05474e |
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.