Defect characterization of electron beam melted Ti-6Al-4V and Alloy 718 with X-ray microtomography

  • Artikel/kapitelEngelska2018

Förlag, utgivningsår, omfång ...

  • 2018-05-18
  • MedCrave Group,2018
  • electronicrdacarrier

Nummerbeteckningar

  • LIBRIS-ID:oai:DiVA.org:ltu-68924
  • https://urn.kb.se/resolve?urn=urn:nbn:se:ltu:diva-68924URI
  • https://doi.org/10.15406/aaoaj.2018.02.00044DOI

Kompletterande språkuppgifter

  • Språk:engelska
  • Sammanfattning på:engelska

Ingår i deldatabas

Klassifikation

  • Ämneskategori:ref swepub-contenttype
  • Ämneskategori:art swepub-publicationtype

Anmärkningar

  • Electron beam melting (EBM) is emerging as a promising manufacturing process where metallic components are manufactured from three-dimensional (3D) computer aided design models by melting layers onto layers. There are several advantages with this manufacturing process such as near net shaping, reduced lead times and the possibility to decrease weight by topology optimization, aspects that are of interest for the aerospace industry. In this work two alloys, Ti-6Al-4V and Alloy 718, widely used within the aerospace industry were investigated with X-ray microtomography (XMT), to characterize defects such as lack of fusion (LOF) and inclusions. It was furthermore possible to view the macrostructure with XMT, which was compared to macrostructure images obtained by light optical microscopy (LOM). XMT proved to be a useful tool for defect characterization and both LOF and un-melted powder could be found in the two investigated samples. In the EBM built Ti-6Al-4V sample high density inclusions, believed to be composed of tungsten, were found. One of the high-density inclusions was found to be hollow, which indicate that the inclusion stems from the powder manufacturing process and not related with the EBM process. By performing defect analyses with the XMT software it was also possible to quantify the amount of LOF and un-melted powder in vol%. From the XMT-data meshes were produced so that finite element method (FEM) simulations could be performed. From these FEM simulations the significant impact of defects on the material properties was evident, as the defects led to high stress concentrations. It could moreover, with FEM, be shown that the as-built surface roughness of EBM material is of importance as high surface roughness led to increased stress concentrations.

Ämnesord och genrebeteckningar

Biuppslag (personer, institutioner, konferenser, titlar ...)

  • Forsberg, FredrikLuleå tekniska universitet,Strömningslära och experimentell mekanik(Swepub:ltu)fred (författare)
  • Pederson, RobertDepartment of Engineering Science, University West (författare)
  • Antti, Marta-LenaLuleå tekniska universitet,Materialvetenskap(Swepub:ltu)marta (författare)
  • Åkerfeldt, PiaLuleå tekniska universitet,Materialvetenskap(Swepub:ltu)piaake (författare)
  • Larsson, SimonLuleå tekniska universitet,Material- och solidmekanik(Swepub:ltu)simlar (författare)
  • Jonsén, Pär,1971-Luleå tekniska universitet,Material- och solidmekanik(Swepub:ltu)parj (författare)
  • Puyoo, GeraldineGKN-Aerospace Engine Systems (författare)
  • Luleå tekniska universitetMaterialvetenskap (creator_code:org_t)

Sammanhörande titlar

  • Ingår i:Aeronautics and Aerospace Open Access Journal: MedCrave Group2:3, s. 139-1452576-4500

Internetlänk

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy