Spinodal Decomposition in Functionally Graded Super Duplex Stainless Steel and Weld Metal

Hosseini, Vahid, 1987- (författare): Högskolan Väst,Avdelningen för svetsteknologi (SV),Innovatum AB Trollhättan,Trollhättan,Sweden,PTW,Innovatum,University West

Thuvander, Mattias, 1968 (författare): Chalmers University of Technology, Department of Physics, Gothenburg,Sweden,PTW,Chalmers tekniska högskola

Wessman, Sten, 1967- (författare): Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW,University West

Karlsson, Leif, 1956- (författare): Högskolan Väst,Avdelningen för svetsteknologi (SV),PTW,University West

(creator_code:org_t)

2018-04-17
2018
Engelska.
Ingår i: Metallurgical and Materials Transactions. A. - : Springer Science and Business Media LLC. - 1073-5623 .- 1543-1940. ; 49A:7, s. 2803-2816

Relaterad länk:: https://doi.org/10.1...; visa fler...; https://hv.diva-port... (primary) (Raw object); https://link.springe...; https://research.cha... (primary) (free); https://urn.kb.se/re...; https://doi.org/10.1...; https://research.cha...; https://research.cha...; visa färre...

Abstract Ämnesord

Stäng

Low-temperature phase separations (T < 500 °C), resulting in changes in mechanical and corrosion properties, of super duplex stainless steel (SDSS) base and weld metals were investigated for short heat treatment times (0.5 to 600 minutes). A novel heat treatment technique, where a stationary arc produces a steady state temperature gradient for selected times, was employed to fabricate functionally graded materials. Three different initial material conditions including 2507 SDSS, remelted 2507 SDSS, and 2509 SDSS weld metal were investigated. Selective etching of ferrite significantly decreased in regions heat treated at 435 °C to 480 °C already after 3 minutes due to rapid phase separations. Atom probe tomography results revealed spinodal decomposition of ferrite and precipitation of Cu particles. Microhardness mapping showed that as-welded microstructure and/or higher Ni content accelerated decomposition. The arc heat treatment technique combined with microhardness mapping and electrolytical etching was found to be a successful approach to evaluate kinetics of low-temperature phase separations in SDSS, particularly at its earlier stages. A time-temperature transformation diagram was proposed showing the kinetics of 475 °C-embrittlement in 2507 SDSS.

TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)
TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Korrosionsteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Av författaren/redakt...: Hosseini, Vahid, ...; Thuvander, Matti ...; Wessman, Sten, 1 ...; Karlsson, Leif, ...

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Bearbetnings yt ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Kemiteknik; och Korrosionsteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.