Manufacture and characterisation of thermoplastic composites made from PLA/hemp co-wrapped hybrid yarn prepregs
-
- Baghaei, Behnaz (författare)
- Högskolan i Borås,Institutionen Ingenjörshögskolan,Polymer Group
-
- Skrifvars, Mikael (författare)
- Högskolan i Borås,Institutionen Ingenjörshögskolan,Polymer Group
-
- Berglin, Lena (författare)
- Högskolan i Borås,Institutionen Textilhögskolan,Polymer Group
-
(creator_code:org_t)
- Elsevier Ltd, 2013
- 2013
- Engelska.
-
Ingår i: Composites. Part A, Applied science and manufacturing. - : Elsevier Ltd. - 1359-835X .- 1878-5840. ; 50, s. 93-101
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- PLA/hemp co-wrapped hybrid yarns were produced by wrapping PLA filaments around a core composed of a 400 twists/m and 25 tex hemp yarn (Cannabis Sativa L) and 18 tex PLA filaments. The hemp content varied between 10 and 45 mass%, and the PLA wrapping density around the core was 150 and 250 turns/metre. Composites were fabricated by compression moulding of 0/90 bidirectional prepregs, and characterised regarding porosity, mechanical strength and thermal properties by dynamic mechanical thermal analysis (DMTA) and differential scanning calorimetry (DSC). Mechanical tests showed that the tensile and flexural strengths of the composites markedly increased with the fibre content, reaching 59.3 and 124.2 MPa when reinforced with 45 mass% fibre, which is approximately 2 and 3.3 times higher compared to neat PLA. Impact strength of the composites decreased initially up to 10 mass% fibre; while higher fibre loading (up to 45 mass%) caused an increase in impact strength up to 26.3 KJ/m2, an improvement of about 2 times higher compared to neat PLA. The composites made from the hybrid yarn with a wrapping density of 250 turns/metre showed improvements in mechanical properties, due to the lower porosity. The fractured surfaces were investigated by scanning electron microscopy to study the fibre/matrix interface.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
- NATURVETENSKAP -- Kemi -- Polymerkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Polymer Chemistry (hsv//eng)
Nyckelord
- Natural fibre composite
- Hybrid yarns
- Mechanical testing
- Compression moulding
- Biocomposites
- Resursåtervinning
- Resource Recovery
- Resursåtervinning
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas