Polyamide 66/clay nanocomposites via melt intercalation
-
- Liu, Xiaohui (author)
- State Key Laboratory of Engineering Plastics, Institute of Chemistry, Chinese Academy of Sciences
-
- Wu, Qiuju (author)
- Luleå tekniska universitet
-
(creator_code:org_t)
- 2002
- 2002
- English.
-
In: Macromolecular materials and engineering. - 1438-7492 .- 1439-2054. ; 287:3, s. 180-186
- Related links:
-
https://urn.kb.se/re...
-
show more...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- Polyamide 66/clay nanocomposites (PA66CN) were prepared via a melt compounding method using a new kind of organophilic clay, which was obtained through co-intercalation of epoxy resin and quaternary ammonium into Na-montmorillonite. The dispersion effect of silicate layers in the matrix was studied by means of XRD and TEM. The silicate layers were dispersed homogeneously and nearly exfoliated in the matrix as a result of the strong interaction between epoxy groups and PA66. The mechanical properties and heat distortion temperature (HDT) of PA66CN increased dramatically. The notched Izod impact strength of PA66CN was 50% higher than that of PA66 when the clay loading was 5 wt.-%. Even at 10 wt.-% clay content, the impact strength was still higher than that of PA66. The finely dispersed silicate layers and the strong interaction between silicate layers and the matrix reduced the water absorption, at 10 wt.-% clay content; PA66CN only absorbs 60% water compared with PA66. The addition of silicate layers changed the crystal structure in PA66CN
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Kompositmaterial och -teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Composite Science and Engineering (hsv//eng)
Keyword
- Polymera konstruktionsmaterial
- Polymeric Composite Materials
Publication and Content Type
- ref (subject category)
- art (subject category)
Find in a library
To the university's database