Influence of MnS inclusion characteristics on generation of white etching cracks in 100Cr6 bearing steel

• Wind turbine gearbox (WTGB) bearings suffer from premature failures through white etching cracks (WECs). To investigate causes of this failure mechanism, we tested two types of 100Cr6 bearing steel components. We carried out rolling contact fatigue experiments on standard washers and material extracted from a WTGB bearing. These differed strongly in morphology and orientation of non-metallic inclusions (NMIs) with respect to the raceway, especially of MnS-type. While the standard washer did not exhibit WECs formation, the WTGB bearing did - even under moderate conditions (1.9 GPa Hertzian pressure, 107 cycles). We therefore conclude that MnS-inclusions are a key factor in initiation of WECs in WTGB bearings.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Tribologi (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Tribology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Electron microscopy

Steel

White etching cracks

Rolling contact fatigue

Bearings

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)