Combustion synthesis and electrochemical performance of Li2FeSiO4/C cathode material for lithium-ion batteries

• A novel preparation technique was developed for synthesizing Li2FeSiO4/C nanoparticles through combustion of reaction mixtures containing silicon source. Li and Fe sources that operate as oxidizers and sucrose that act as a fuel. A systematic investigation of the synthesis parameters, such as the effect of the fuel content, on purity, morphology and electrochemical properties of the samples was performed. The samples were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), specific surface area (BET) and electrochemical measurements, respectively. Among the synthesized cathode materials, Li2FeSiO4 obtained with 1.5 mol of sucrose, showed the best electrochemical performance in terms of discharge capacity, cycling stability and rate capability. Discharge capacity of 130 mAh/g at C/20, 88 mAh/g at C/2 and 44 mAh/g at 2C were obtained with no capacity fading after 50 cycles.

Subject headings

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

Keyword

Lithium-ion batteries

Lithium iron orthosilicate

Combustion synthesis

Inorganic chemistry

Oorganisk kemi

Kemi med inriktning mot oorganisk kemi

Chemistry with specialization in Inorganic Chemistry

Publication and Content Type

ref (subject category)

art (subject category)