Solid solution softening at room temperature and hardening at elevated temperatures: a case by minor Mn addition in a (HfNbTi) 85 Mo 15 refractory high entropy alloy

• To address the conflict between room-temperature (RT) ductility and high-temperature (HT) strength in single phase bcc-structured refractory high entropy alloys, here we propose to use minor alloying to achieve solid solution softening at RT and simultaneously, solid solution hardening at HT. Our strategy was manifested by minor Mn additions in a RT brittle (HfNbTi)85Mo15 refractory high entropy alloy, where nominal Mn additions ranging from 2 at. % down to 0.03 at. % were seen to soften the base (HfNbTi)85Mo15 alloy at RT, while to harden the base alloy at the temperature range from 400 to 800 °C. The yield stress in all studied alloys showed a three-stage pattern, characterized by a temperature dependent stage at temperatures below 400 °C, followed by a temperature independent stage at intermediate temperatures ranging from 400 to 800 °C, and finally another temperature dependent stage at temperatures higher than 800 °C. The mechanisms for solid solution softening and solid solution hardening in single phase bcc-structured refractory high entropy alloys were discussed, together with their temperature dependence.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

solid solutions

refractory high entropy alloys

solid solution softening and hardening

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)