100 | 1 | a Cho, C. R.4 aut |
245 | 1 0 | a Na0.5K0.5NbO3 thin films for MFIS_FET type non-volatile memory applications |
264 | 1 | c 2002 |
338 | a print2 rdacarrier | |
500 | a QC 20100525 | |
520 | a Na0.5K0.5NbO3(NKN) thin films have been prepared on Pt80Ir20, SiO2/Si, and Ta2O5/Si substrates for ferroelectric non-volatile memory applications. Ferroelectric hysteresis loops for Au/NKN/Pt80Ir20 vertical capacitor yielded remnant polarization of 12 muC/cm(2) and coercive field similar to20 kV/cm. Significant flat-band voltage V-FB shifts with buffer layer thickness in Au/NKN/SiO2/Si structures have been attributed to the intermixing between Na and K alkali ions and SiO2 layer. On the other hand, Au/NKN/Ta2O5/Si structure exhibited wide memory window without significant V-FB deviations, low leakage currents, and rather long retention time at zero bias. | |
653 | a Na0.5K0.5NbO3 (NKN) thin film | |
653 | a Au/NKN/Ta2O5/Si | |
653 | a MFIS_diode | |
653 | a ferroelectric non-volatile memory | |
653 | a pulsed-laser deposition | |
653 | a varactor | |
700 | 1 | a Park, S. H.4 aut |
700 | 1 | a Moon, B. M.4 aut |
700 | 1 | a Sundqvist, J.4 aut |
700 | 1 | a Harsta, A.4 aut |
700 | 1 | a Grishin, Alexander M.u KTH,Mikroelektronik och informationsteknik, IMIT4 aut0 (Swepub:kth)u179x9xt |
710 | 2 | a KTHb Mikroelektronik och informationsteknik, IMIT4 org |
773 | 0 | t Integrated Ferroelectricsg 49, s. 21-30q 49<21-30x 1058-4587x 1607-8489 |
856 | 4 8 | u https://urn.kb.se/resolve?urn=urn:nbn:se:kth:diva-22120 |
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
Kopiera och spara länken för att återkomma till aktuell vy