Ambient air-processed mixed-ion perovskites for high-efficiency solar cells
-
- Sveinbjörnsson, Kári (författare)
- Uppsala universitet,Fysikalisk kemi
-
- Aitola, Kerttu (författare)
- Uppsala universitet,Fysikalisk kemi
-
- Zhang, Jinbao (författare)
- Uppsala universitet,Fysikalisk kemi
-
visa fler...
-
- Johansson, Malin B. (författare)
- Uppsala universitet,Fysikalisk kemi
-
- Zhang, Xiaoliang (författare)
- Uppsala universitet,Fysikalisk kemi
-
- Correa-Baena, Juan-Pablo (författare)
- Ecole Polytech Fed Lausanne, Lab Photomol Sci, EPFL SB ISIC LSPM, CH G1 523,Chemin Alamb,Stn 6, CH-1015 Lausanne, Switzerland.
-
- Hagfeldt, Anders (författare)
- Ecole Polytech Fed Lausanne, Lab Photomol Sci, EPFL SB ISIC LSPM, CH G1 523,Chemin Alamb,Stn 6, CH-1015 Lausanne, Switzerland.
-
- Boschloo, Gerrit (författare)
- Uppsala universitet,Fysikalisk kemi,Uppsala Univ, Dept Chem, Angstrom Lab, Phys Chem, Box 523, S-75120 Uppsala, Sweden.
-
- Johansson, Erik M. J. (författare)
- Uppsala universitet,Fysikalisk kemi
-
visa färre...
-
(creator_code:org_t)
- 2016
- 2016
- Engelska.
-
Ingår i: Journal of Materials Chemistry A. - : Royal Society of Chemistry (RSC). - 2050-7488 .- 2050-7496. ; 4:42, s. 16536-16545
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Mixed-ion (FAPbI(3))(1-x)(MAPbBr(3))(x) perovskite solar cells have achieved power conversion efficiencies surpassing 20%. However, in order to obtain these high efficiencies the preparation is performed in a controlled inert atmosphere. Here, we report a procedure for manufacturing highly efficient solar cells with a mixed-ion perovskite in ambient atmosphere. By including a heating step at moderate temperatures of the mesoporous titanium dioxide substrates, and spin-coating the perovskite solution on the warm substrates in ambient air, a red intermediate phase is obtained. Annealing the red phase at 100 degrees C results in a uniform and crystalline perovskite film, whose thickness is dependent on the substrate temperature prior to spin-coating. The temperature was optimized between 20 and 100 degrees C and it was observed that 50 degrees C substrate temperature yielded the best solar cell performances. The average efficiency of the best device was 17.6%, accounting for current-voltage (I-V) measurement hysteresis, with 18.8% performance in the backward scan direction and 16.4% in the forward scan direction. Our results show that it is possible to manufacture high-efficiency mixed-ion perovskite solar cells under ambient conditions, which is relevant for large-scale and low-cost device manufacturing processing.
Ämnesord
- NATURVETENSKAP -- Kemi -- Fysikalisk kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Physical Chemistry (hsv//eng)
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas