An investigation of the corrosion resistances of magnetron sputtered TaW-rich, Nb-rich, and multicomponent CrNbTaTiW alloys

Srinath, Aishwarya, 1991- (författare)
Uppsala universitet,Oorganisk kemi,Inorganic Chemistry
Fritze, Stefan (författare)
Korvela, Marcus (författare)
visa fler...
Rehnlund, David (författare)
Malinovskis, Paulius (författare)
von Fieandt, Kristina (författare)
Pan, Ruijun (författare)
Pettersson, Jean (författare)
Sternhagen, Victoria (författare)
Riekehr, Lars (författare)
Lewin, Erik (författare)
Lindblad, Rebecka (författare)
Jansson, Ulf (författare)
Nyholm, Leif (författare)
visa färre...
 (creator_code:org_t)
Engelska.
Relaterad länk:
https://urn.kb.se/re...
  • Annan publikation (övrigt vetenskapligt/konstnärligt)
Abstract Ämnesord
Stäng  
  • The corrosion resistances of magnetron sputtered nearequimolar, TaW-rich, and Nb-rich CrNbTiTaW alloys, with and without 8 at.% carbon, were studied in aqueous chloride-containing environments. Electrochemical tests and scanning electron images showed that all the CrNbTaTiW alloys were highly corrosion resistant in 1.0 M HCl. The results conclusively showed that passivated nearequimolar CrNbTaTiW coatings have comparable corrosion performances to passivated Nb- and TaW-rich alloys in 0.01 M HCl + 0.1 M NaCl. Carbon affected the rate of surface repassivation in polarisation measurements of the films whose oxide had been partially reduced, but had a minor influenceon the corrosion resistances once a mature oxide was formed. No conclusive relationships between microstructure and corrosion resistance were established. The comparable corrosion resistances of the multicomponent CrNbTiTaW, Nb-rich and TaW-rich alloys were attributed to the presence of extremely stable surface oxides of Nb and Ta which prevented losses of Ti and Cr. The near surface regions of all the alloys before and after corrosion appeared to be depleted in W compared to the bulk.

Ämnesord

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Corrosion
Kemi med inriktning mot materialkemi
Chemistry with specialization in Materials Chemistry

Publikations- och innehållstyp

vet (ämneskategori)
ovr (ämneskategori)

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy