Electric fatigue in antiferroelectric lead zirconate stannate titanate ceramics prepared by spark plasma sintering

QC 20120302
The fatigue behavior of lead zirconate stannate titanate (PZST) ceramics prepared by spark plasma sintering (SPS) was investigated. Polarization and strain hysteresis loops were monitored. The material shows a high resistance to fatigue because of bipolar electric cycling. Both maximum strain and switchable polarization first show a fatigue stage 0 to 10(5) cycles and then a fatigue-free period up to 10(8) cycles. The maximum losses of maximum strain and switchable polarization are 18% and 10% of their initial values, respectively. The dominant fatigue mechanism is assigned to the pinning of domain walls by charged defects.

Rixecker, G. (författare)
Zimmermann, A. (författare)
Aldinger, F. (författare)
Zhao, Zhe,1973-Department of Physical Inorganic and Structural Chemistry, Stockholm University(Swepub:kth)u1qw3zev (författare)
Nygren, M. (författare)
Department of Physical Inorganic and Structural Chemistry, Stockholm University (creator_code:org_t)

Ingår i:Journal of The American Ceramic Society: American Ceramic Society88:10, s. 2952-29540002-78201551-2916
Ingår i:International Studies Review: American Ceramic Society88:10, s. 2952-29541521-94881468-2486

Av författaren/redakt...: Zhou, L. J.; Rixecker, G.; Zimmermann, A.; Aldinger, F.; Zhao, Zhe, 1973-; Nygren, M.

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Keramteknik

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.