Effect of Boron and Cross-Section Thickness on Microstructure and Mechanical Properties of Ductile Iron
-
- Kasvayee, Keivan Amiri, 1986- (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Ciavatta, Matteo (författare)
- University of Bologna, Bologna, Italy
-
- Ghassemali, Ehsan, 1983- (författare)
- Jönköping University,JTH, Material och tillverkning
-
visa fler...
-
- Svensson, Ingvar L. (författare)
- Jönköping University,JTH, Material och tillverkning
-
- Jarfors, Anders E.W. 1963- (författare)
- Jönköping University,JTH, Material och tillverkning
-
visa färre...
-
(creator_code:org_t)
- Trans Tech Publications, 2018
- 2018
- Engelska.
-
Ingår i: Materials Science Forum. - : Trans Tech Publications. - 0255-5476 .- 1662-9752. ; 925, s. 249-256
- Relaterad länk:
-
https://doi.org/10.4...
-
visa fler...
-
https://www.scientif...
-
https://urn.kb.se/re...
-
https://doi.org/10.4...
-
visa färre...
Abstract
Ämnesord
Stäng
- Eeffect of Boron addition on the microstructure and mechanical properties of ductile iron, GJS-500-7 grade was studied. Three cast batches with the Boron content of 10, 49 and 131ppm were cast in a casting geometry containing plates with thicknesses of 7, 15, 30, 50 and 75mm. Microstructure analysis, tensile test, and hardness test were performed on the samples which were machined from the casting plates. Addition of 49 ppm Boron decreased pearlite fraction by an average of 34±6% in all the cast plates. However, minor changes were observed in the pearlite fraction by increasing Boron from 49 to 131 ppm. Variation in the plate thickness did not affect the pearlite fraction. The 0.2% offset yield and ultimate tensile strength was decreased by an average of 11±1% and 18±2%, respectively. Addition of 49 ppm Boron decreased Brinell hardness by 16±1%, while 11±2% reduction was obtained by addition of 131ppm Boron.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Nyckelord
- Boron
- Component Casting
- Ductile Iron
- Hardness
- Mechanical Properties
- Spherical Graphite Iron