Fracture Mechanics of Gray Cast Iron
-
- Diószegi, Attila (författare)
- Jönköping University,JTH. Forskningsområde Material och tillverkning - gjutning,JTH, Maskinteknik
-
- Fourlakidis, Vasilios (författare)
- RISE,SWECAST,Swerea - Swecast
-
- Svensson, Ingvar L (författare)
- Jönköping University,JTH. Forskningsområde Material och tillverkning - gjutning,JTH, Maskinteknik
-
Jönköping University JTH Forskningsområde Material och tillverkning - gjutning (creator_code:org_t)
- Trans Tech Publication, Switzerland, 2010
- 2010
- Engelska.
-
Serie: Materials Engineering Forum ; 649
-
Ingår i: Materials Science Forum. - : Trans Tech Publication, Switzerland. - 0255-5476 .- 1662-9752. ; 649, s. 517-522
- Relaterad länk:
-
http://www.scopus.co...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.4...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The fracture mechanism of gray cast iron was investigated on tension loaded samples produced under different conditions. The parameters studied included the graphite morphology, the carbon content, the inoculation and the cooling condition. The observations made reveal the role of the microstructure on crack propagation. The cracks were found to always propagate parallel with the graphite flakes. The interaction between the metallic matrix precipitated as primary austenite and graphite has been interpreted by a simplified model of the austenite reinforced eutectic cell. The geometrical transcription gave a standard crack component configuration with known mathematical solution. The microstructure observed in the experiments has been analysed by means of a novel interpretation. The fictitious stress intensity at yield and the fictitious maximum stress intensity at failure are strongly related to the relative shape of the eutectic cell and the fraction primary austenite. A different slope is observed for the material cooled at high rate when the precipitation of primary carbide reduces the stress intensity. The observed relations indicate that the tensile strength of the grey cast iron is the result of the collaboration between the toughness of the metallic matrix precipitated as primary austenite and the brittleness of the graphite phase. The shape and distribution of the primary austenite and graphite can be influenced by chemical composition, by inoculation or by the cooling condition, but they will maintain equilibrium with respect to the stress intensity.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Nyckelord
- fracture mechanism
- gray cast iron
- primary austenite
- eutectic cell
- TECHNOLOGY
- TEKNIKVETENSKAP
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas