Deposition and mechanical properties of polycrystalline Y2O3/ZrO2 superlattices
-
- Yashar, PC (författare)
- Northwestern Univ, Dept Mat Sci & Engn, Evanston, IL 60208 USA Linkoping Univ, Dept Phys, Thin Film Phys Div, S-58183 Linkoping, Sweden Northwestern Univ, Adv Coatings Technol Grp, Evanston, IL 60201 USA
-
- Barnett, SA (författare)
- Northwestern Univ, Dept Mat Sci & Engn, Evanston, IL 60208 USA Linkoping Univ, Dept Phys, Thin Film Phys Div, S-58183 Linkoping, Sweden Northwestern Univ, Adv Coatings Technol Grp, Evanston, IL 60201 USA
-
- Hultman, Lars (författare)
- Linköpings universitet,Tekniska högskolan,Tunnfilmsfysik
- visa fler...
- visa färre...
- (creator_code:org_t)
- 1999
- 1999
- Engelska.
- Ingår i: Journal of Materials Research. - 0884-2914 .- 2044-5326. ; 14:9, s. 3614-3622
- Tidskriftsartikel (refereegranskat)
Abstract
Ämnesord
Stäng
- Polycrystalline Y2O3/ZrO2 superlattice thin films were deposited using opposed-cathode reactive magnetron sputtering. Pulsed direct-current power was used to eliminate arcing on the metallic targets. Radio-frequency power was applied to the substrates to achieve ion bombardment of the growing film. In order to reproducibly deposit at high rates in Ar-O-2 mixtures, the Y target voltage was used to indirectly feedback-control the O-2 partial pressure. Deposition rates as high as similar to 70% of the pure metal rates were achieved, typically 3.5 mu m/h. Superlattices with periods ranging from 2.6 to 95 nm were deposited. Y2O3 layer thicknesses were either 75% or 50% of the superlattice period. X-ray diffraction and transmission electron microscopy studies showed well-defined superlattice layers. The ZrO2 layers exhibited the high-temperature cubic-fluorite structure, which was epitaxially stabilized by the cubic Y2O3 layers, for thicknesses less than or equal to 7 nm. The equilibrium monoclinic structure was observed for thicker ZrO2 layers. Nanoindentation hardnesses ranged from 11.1 to 14.5 GPa with little dependence on period. The hardness results are discussed in terms of current superlattice hardening theories.
Nyckelord
- TECHNOLOGY
- TEKNIKVETENSKAP
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
- Journal of Materials Research (Sök värdpublikationen i LIBRIS)
Till lärosätets databas
Hitta mer i SwePub
- Av författaren/redakt...
- Yashar, PC
- Barnett, SA
- Hultman, Lars
- Sproul, WD
- Artiklar i publikationen
- Journal of Mater ...
- Av lärosätet
- Linköpings universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se