A Study of Nitrogen Pickup from the Slag during Waiting Time of Ladle Treatment

Sökning: L773:1611 3683 > A Study of Nitrogen...

Kojola, Niklas (författare)

Hui, Wang (författare)

(creator_code:org_t)

2013-08-12
2014
Engelska.
Ingår i: Steel Research International. - : Wiley. - 1611-3683 .- 1869-344X. ; 85:4, s. 689-696

Relaterad länk:: https://urn.kb.se/re...; visa fler...; https://doi.org/10.1...; visa färre...

Abstract Ämnesord

Stäng

An investigation of the nitrogen pickup of liquid steel from ladle slag after vacuum degassing was made. Nitride capacities, C-N, of a number of ladle slags were determined at controlled nitrogen and oxygen potentials at 1873K. The nitride capacities in the composition range studied were found to be very low. In accordance with the literature, the nitride capacity was found to increase with increasing SiO2 content. Industrial trials were performed. The nitrogen content of the steel was determined before and after vacuum degassing as well as after the waiting period. Three different trends of the variation of nitrogen content in the steel were observed. Both the laboratory study and the industrial trials revealed that the transfer of nitrogen from slag to steel was not the reason for nitrogen pickup in the steel subsequent to vacuum degassing.

Av författaren/redakt...: Allertz, Carl; Kojola, Niklas; Hui, Wang; Sichen, Du

Om ämnet

TEKNIK OCH TEKNOLOGIER: TEKNIK OCH TEKNO ...; och Materialteknik; och Metallurgi och m ...

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.