Electrochemical characterization of poly(vinylidene fluoride-co-hexafluoro propylene) based electrospun gel polymer electrolytes incorporating moth temperature ionic liquids as green electrolytes for lithium batteries
-
- Raghavan, P. (författare)
- Gyeongsang National University
-
- Zhao, X. (författare)
- Gyeongsang National University
-
- Choi, H. (författare)
- Gyeongsang National University
-
visa fler...
-
- Lim, Du Hyun, 1983 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Kim, Jae-Kwang, 1978 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Matic, Aleksandar, 1968 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Jacobsson, Per, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Nah, C. (författare)
- Chonbuk National University
-
- Ahn, J. H. (författare)
- Gyeongsang National University
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2014
- 2014
- Engelska.
-
Ingår i: Solid State Ionics. - : Elsevier BV. - 0167-2738. ; 262, s. 77-82
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- A series of gel polymer electrolytes (GPEs) based on electrospun membranes of poly(vinylidene fluoride-co-hexafluoropropylene) [P(VdF-co-HFP)] incorporating room temperature ionic liquids (RTILs), 1-alkyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide complexed with lithium bis(trifluoromethylsulfonyl) inside (LiTFSI) as electrolytes have been prepared and their fundamental electrochemical properties were investigated. The morphology of electrospun membranes was examined by a field emission scanning electron microscope (FE-SEM). The membranes show uniform morphology with an average fiber diameter of 780 nm, high porosity and high electrolyte uptake. GPEs were prepared by soaking the electrospun membranes in 1 M LiTFSI in RTILs for 1 h and exhibit a high ionic conductivity of 2.4 x 10(-3)-4.5 x 10(-3) S cm(-1) at 25 degrees C. A Li/GPEs/LiFePO4 cell using these RTILs delivers high discharge capacity (similar to 140 mAh g(-1)) when evaluated at 25 degrees C at 0.1 C-rate and exhibits a very stable discharge capacity under continuous cycling. Among the GPEs, EMITFSI shows the highest electrochemical properties although the solid electrolyte interface (SEI) layer was not formed.
Ämnesord
- NATURVETENSKAP -- Fysik -- Den kondenserade materiens fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences -- Condensed Matter Physics (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Raghavan, P.
-
Zhao, X.
-
Choi, H.
-
Lim, Du Hyun, 19 ...
-
Kim, Jae-Kwang, ...
-
Matic, Aleksanda ...
-
visa fler...
-
Jacobsson, Per, ...
-
Nah, C.
-
Ahn, J. H.
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Fysik
-
och Den kondenserade ...
- Artiklar i publikationen
-
Solid State Ioni ...
- Av lärosätet
-
Chalmers tekniska högskola